| Curing agents for Epoxy resins. |
| BONTAMINE (MODIFIED AMINE) （Epoxy resin curing
agent） |
| Item
number |
Amine
Value |
viscocity
CPS/25℃ |
Color
MAX |
H.ACIVE
E.W. AHEW |
Mixing
ratio
PHR
EEW=190 |
Pot
life(min)
25℃/100g |
Application |
PROPERTY |
| Adhesive
|
Lamination
|
Casting |
Paint |
Civil
engineering |
| 5010 |
120±30 |
10000-14000 |
4 |
190 |
100 |
(10g)
3-5 |
0 |
|
|
|
|
5-minutes cure type good flexibility. |
| 5020 |
260±30 |
10000-13000 |
2 |
190 |
100 |
(50g)
10 |
0 |
|
|
0 |
|
Fast cured adhesive, water resistance. |
| 5110 |
290±30 |
500-900 |
2 |
100 |
50 |
42 |
|
0 |
|
0 |
0 |
Colorless, non-solvent, coating, Casting. |
| 5120 |
260±30 |
400-600 |
3 |
90 |
50 |
23 |
|
0 |
|
0 |
0 |
Glssy, excellent hardness, long pot life. |
| 5130 |
310±30 |
200-400 |
3 |
90 |
50 |
38 |
|
0 |
|
0 |
0 |
Excellent top floor coation, long pot life. |
| 5140 |
340±30 |
200-400 |
3 |
90 |
50 |
30 |
|
0 |
|
0 |
0 |
Haze-proof at low and high temperature.
Excellent physical properties. |
| 5210 |
760±30 |
200-400 |
4 |
45 |
25 |
35 |
|
0 |
|
|
0 |
Fast curing resin mortar. |
| 5220 |
750±30
|
200-400
|
8 |
60 |
33 |
26 |
|
0 |
|
|
0 |
Crack bonding of primer in
moisture surface. |
| 5230 |
540±30 |
100-300 |
6 |
57 |
33 |
8 |
0 |
|
|
0 |
0 |
Low temperature curing wet surface curing. |
| 5232 |
350±30 |
800-1500 |
6 |
90 |
50 |
11 |
|
|
|
0 |
0 |
Similar to #5230 ezcellent toughness. |
| 5240 |
550±30 |
300-500 |
6 |
80 |
50 |
24 |
|
0 |
0 |
|
0 |
Fast curing resin mortar, non amine blushing. |
| 5250 |
410±30 |
800-1300 |
8 |
90 |
50 |
4 |
|
|
|
0 |
0 |
Crack bonding of primer in wet condition. |
| 5310 |
|
1500-2500 |
10 |
90 |
50 |
32 |
0 |
|
0 |
0 |
0 |
Excellent acid corrosion resistance, good
electrical insulation. |
| 5320 |
|
500-800 |
10 |
90 |
50 |
38 |
0 |
|
0 |
0 |
0 |
Similar to #5310, low viscosity high hardness. |
| 5330 |
|
1500-2500 |
10 |
110 |
50 |
130 |
0 |
|
0 |
0 |
0 |
Similar to #5310, long pot life, coating
lining. |
| 5340 |
|
200-400 |
10 |
100 |
50 |
20 |
0 |
|
0 |
0 |
0 |
Good acid resistance, good encapsulation.
With tar and asphalt. |
| 5360 |
|
1500-2500 |
10 |
100 |
50 |
70 |
0 |
|
0 |
0 |
0 |
Same as above, harden rapidly. |
| 5410 |
550±30 |
60-150 |
8 |
44 |
25 |
84 |
|
|
0 |
|
|
High temperature resistant. HDT=150℃ |
| 5420 |
550±30 |
700-1500 |
4 |
60 |
30 |
30 |
0 |
|
|
0 |
|
Heat resisting HDT=110℃ |
| 5430 |
170±30 |
60000-80000 |
10 |
30 |
20 |
24hr |
0 |
|
0 |
|
|
Quick harden by heating. Heat resistance. |
| 5510 |
|
50-100 |
3 |
160 |
85 |
180 |
|
|
0 |
|
|
Heat hardening type, heat resistance, high
electrical performance. |
| 5610 |
280±30 |
100-200 |
2 |
100 |
33 |
55 |
|
|
0 |
|
|
Mixed with 5610 A to obtain softer resin. |
| 5620 |
450±30 |
10-30 |
2 |
60 |
30 |
6hr |
|
0 |
0 |
|
|
Low viscosity, high electrical performance.
Accesory casting and adhesive. |
| 5630 |
250±30 |
20-50 |
2 |
100 |
50 |
8hr |
|
0 |
0 |
|
|
Low viscosity, excellent elasticity, longer
pot life. |
| 5640 |
330±30 |
30-50 |
2 |
75 |
33 |
74 |
|
0 |
0 |
|
|
Low viscosity, high electrical performance.
Accesory casting. |
|
| |
| BONTAMIDE (POLYAMIDE RESIN)（Epoxy resin curing
agent） |
|
Item number
|
Amine Value
|
viscocity
CPS/25℃
|
Color
MAX
|
Active hydrogen equivalent
|
Mixing ratio
PHR
EEW=190
|
Pot life(min)
25℃/100g
|
Application
|
Characteristics
|
|
Adhesive
|
Lamination
|
Casting
|
Paint
|
Civil engineering
|
|
2010
|
210±30
|
(40℃)
50000-70000
|
8
|
180
|
100
|
360
|
○
|
○
|
|
○
|
|
Water resistance, oil-proof,
chemical resistance. |
|
2020
|
240±30
|
(40℃)
30000-50000
|
8
|
150
|
100
|
140
|
○
|
○
|
|
○
|
|
High viscosity, excellent adhesivity,
used together with 2010 for zink paint. |
|
2030
|
310±30
|
(40℃)
9000-14000
|
8
|
125
|
100
|
100
|
○
|
○
|
|
○
|
○
|
Standard type, adhesive, good
tenacity. |
|
2031
|
270±30
|
(40℃)
9000-14000
|
8
|
125
|
100
|
70
|
○
|
○
|
|
○
|
○
|
Same as above, less stink odor. |
|
2032
|
250±30
|
(40℃)
14000-24000
|
8
|
150
|
100
|
45
|
○
|
○
|
|
○
|
○
|
Same as above, faster post-hardening. |
|
2040
|
360±30
|
6000-10000
|
8
|
120
|
50
|
100
|
○
|
○
|
|
○
|
|
Aqueous emulsion, non-sagging
when used on walls. |
|
2050
|
350±30
|
10000-15000
|
8
|
100
|
50
|
136
|
○
|
○
|
|
○
|
○
|
High tenacity, longer pot-life.
Good for grinder. |
|
2060
|
320±30
|
6000-12000
|
8
|
110
|
50
|
28
|
○
|
|
○
|
○
|
|
Cure at low temperature and in
water. Suitable for adhering new mortar to old one. |
|
2070
|
400±30
|
25000-35000
|
8
|
90
|
50
|
100
|
○
|
○
|
○
|
|
○
|
Longer pot-life, moderafe viscosity,
good for resin slurry. |
|
2080
|
400±30
|
1500-3000
|
8
|
80
|
50
|
73
|
○
|
○
|
○
|
|
○
|
Same as above, good for winter
season. |
|
2085
|
340±20
|
1000-1500
|
8
|
110
|
100
|
50
|
○
|
|
○
|
○
|
|
High tenacity, impact resistance. |
|
2090
|
330±20
|
500-800
|
8
|
120
|
50
|
190
|
○
|
|
○
|
|
|
Low heat, low viscosity. Longer
pot life. |
|
2100
|
390±30
|
300-500
|
10
|
100
|
50
|
120
|
|
|
○
|
○
|
|
Low viscosity, Longer pot
life. |
|
2105
|
380±30
|
400-600
|
10
|
100
|
50
|
84
|
○
|
○
|
○
|
○
|
|
Same as above, faster hardening,
for resin slurry. |
|
2110
|
560±30
|
1500-2500
|
10
|
80
|
45
|
23
|
○
|
|
○
|
○
|
|
High reactive curing agent. |
|
2120
|
750±30
|
300-500
|
10
|
45
|
25
|
30
|
○
|
|
○
|
○
|
○
|
Low viscosity, harden quickly,
excellent chemical resistance. |
|
2210
|
150±30
|
1500-3000
|
6
|
240
|
120
|
70%
|
|
|
|
○
|
|
Chemical resistance, good for
low temperature. Excellent metal adhesivity. |
|
2230
|
200±30
|
200-500
|
6
|
170
|
EEW=450
|
60%
|
|
|
|
○
|
|
Water-proof, good for wet surface,
excellent adhesivity. |
|
2310
|
350±30
|
Non-sagging paste
|
10
|
100
|
50
|
60
|
○
|
|
|
|
|
Non-sagging, high thixotropy,
excellent adhesiveness. |
|
2320
|
230±30
|
(45℃)
4000-8000
|
8
|
180
|
100
|
30
|
○
|
|
|
|
|
For special surface adhesive,
high peeling strength, impact resistance. |
|
|